Availability includes Monolith, and random packed medias, such as Ceramic Saddles, Raschig Rings, Mini-Rings, Honeycomb & Triangular shapes, Porcelain Balls, and Cell Stone® ULTRA random packed saddles.

With so many options to choose from, one is surely appropriate for your application.
 
 
CHEMICAL ANALYSIS LOW DENSITY MONOLITH

COMPOSITION

VALUE

COMPOSITION

VALUE

SiO 2

48-51

Fe 2 O 3

<0.5

Al 2 O 3

31-34

Na 2 O

<0.5

MgO

14-16

K 2 O

<0.5

       
       
DIMENSIONAL DATA LOW DENSITY MONOLITH

DIMENSION

QUANTITY OF CHANNELS

WALL THICKNESS

INNER SURFACE AREA

FREE SPACE

AVERAGE WEIGHT (MIN)

AVERAGE WEIGHT (MIN) LB./F3

150*150*300

60*60

0.5mm

1335 m 2 /m 3

70%

680kg/M 3

42.45

150*150*300

50*50

0.7mm

1005 m 2 /m 3

58%

680kg/M 3

42.45

150*150*300

40*40

0.7mm

825 m 2 /m 3

65%

518kg/M 3

36.27

150*150*300

25*25

1.0mm

540 m 2 /m 3

67%

502 kg/M 3

31.33

             
             
CHEMICAL COMPOSITION HIGH DENSITY MONOLITH

COMPOSITION

VALUE

COMPOSITION

VALUE

SiO 2

48-50%

Fe 2 O 3

<1%

Al 2 O 3

37-39%

Na 2 O

<1%

MgO

7-9%

K 2 O+CaO

<2%

       
       
DIMENSIONAL DATA HIGH DENSITY MONOLITH

DIMENSION

QUANTITY OF CHANNELS

WALL THICKNESS

INNER SURFACE AREA

FREE SPACE

AVERAGE WEIGHT(MIN)

AVERAGE

WEIGHT (MIN) LB./F3

150*150*300

60*60

0.5mm

1335m 2 /m 3

70%

800kg/m 3

49.92

150*150*300

50*50

0.7mm

1005m 2 /m 3

58%

760kg/m 3

47.44

150*150*300

40*40

0.7mm

825m 2 /m 3

65%

740kg/m 3

46.20

150*150*300

25*25

1.0mm

540 m 2 /m 3

67%

680 kg/m 3

42.45